| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| PL Peak | X₀ | 1.65eV | — | |||
| PL Peak | X* | 1.62eV | — | |||
| PL Peak | X₀ | 1.64eV | — | |||
| Pl Peak Shift | X₀ redshift | 10meV | — | |||
| PL Peak | X₀ | 1.65eV | — | |||
| PL Peak | X* | 1.62eV | — | |||
| Pl Peak Shift | PL quenching relative to reference | none significant | — | |||
| PL Peak | X* | reduced spectral weight | — | |||
| Pl Peak Intensity | X₀ | more than one order of magnitude lower than reference | — | |||
| Pl Peak Intensity | X₀ | no significant quenching relative to reference | — | |||
| PL Peak | TRPL decay time | 8.9ps | — | |||
| PL Peak | TRPL decay time | 2ps | — | |||
| PL Peak | exciton transfer time | 2.8ps | — | |||
| PL Peak | exciton transfer time | 2.2-2.4ps | — | |||
| PL Peak | rise time | sub-picosecondps | — | |||
| PL Peak | rise time | sub-picosecondps | — | |||
| PL Peak | hBN spacer thickness | 0.7nm | — | |||
| PL Peak | hBN spacer thickness | 1.7nm | — |
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| PL Peak | X₀ | 1.65eV | — | |||
| PL Peak | X* | 1.62eV | — | |||
| PL Peak | X₀ | 1.64eV | — | |||
| Pl Peak Shift | X₀ redshift | 10meV | — | |||
| PL Peak | X₀ | 1.65eV | — | |||
| PL Peak | X* | 1.62eV | — | |||
| Pl Peak Shift | PL quenching relative to reference | none significant | — | |||
| PL Peak | X* | reduced spectral weight | — | |||
| Pl Peak Intensity | X₀ | more than one order of magnitude lower than reference | — | |||
| Pl Peak Intensity | X₀ | no significant quenching relative to reference | — | |||
| PL Peak | TRPL decay time | 8.9ps | — | |||
| PL Peak | TRPL decay time | 2ps | — | |||
| PL Peak | exciton transfer time | 2.8ps | — | |||
| PL Peak | exciton transfer time | 2.2-2.4ps | — | |||
| PL Peak | rise time | sub-picosecondps | — | |||
| PL Peak | rise time | sub-picosecondps | — | |||
| PL Peak | hBN spacer thickness | 0.7nm | — | |||
| PL Peak | hBN spacer thickness | 1.7nm | — |
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| PL Peak | X₀ | 1.65eV | — | |||
| PL Peak | X* | 1.62eV | — | |||
| PL Peak | X₀ | 1.64eV | — | |||
| Pl Peak Shift | X₀ redshift | 10meV | — | |||
| PL Peak | X₀ | 1.65eV | — | |||
| PL Peak | X* | 1.62eV | — | |||
| Pl Peak Shift | PL quenching relative to reference | none significant | — | |||
| PL Peak | X* | reduced spectral weight | — | |||
| Pl Peak Intensity | X₀ | more than one order of magnitude lower than reference | — | |||
| Pl Peak Intensity | X₀ | no significant quenching relative to reference | — | |||
| PL Peak | TRPL decay time | 8.9ps | — | |||
| PL Peak | TRPL decay time | 2ps | — | |||
| PL Peak | exciton transfer time | 2.8ps | — | |||
| PL Peak | exciton transfer time | 2.2-2.4ps | — | |||
| PL Peak | rise time | sub-picosecondps | — | |||
| PL Peak | rise time | sub-picosecondps | — | |||
| PL Peak | hBN spacer thickness | 0.7nm | — | |||
| PL Peak | hBN spacer thickness | 1.7nm | — |
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| PL Peak | X₀ | 1.65eV | — | |||
| PL Peak | X* | 1.62eV | — | |||
| PL Peak | X₀ | 1.64eV | — | |||
| Pl Peak Shift | X₀ redshift | 10meV | — | |||
| PL Peak | X₀ | 1.65eV | — | |||
| PL Peak | X* | 1.62eV | — | |||
| Pl Peak Shift | PL quenching relative to reference | none significant | — | |||
| PL Peak | X* | reduced spectral weight | — | |||
| Pl Peak Intensity | X₀ | more than one order of magnitude lower than reference | — | |||
| Pl Peak Intensity | X₀ | no significant quenching relative to reference | — | |||
| PL Peak | TRPL decay time | 8.9ps | — | |||
| PL Peak | TRPL decay time | 2ps | — | |||
| PL Peak | exciton transfer time | 2.8ps | — | |||
| PL Peak | exciton transfer time | 2.2-2.4ps | — | |||
| PL Peak | rise time | sub-picosecondps | — | |||
| PL Peak | rise time | sub-picosecondps | — | |||
| PL Peak | hBN spacer thickness | 0.7nm | — | |||
| PL Peak | hBN spacer thickness | 1.7nm | — |
figure_digitization.json#Figure 2figure_digitization.json#Figure S12figure_digitization.json#Figure S14(c)figure_digitization.json#Figure S15(a)figure_digitization.json#Figure S15(b)figure_digitization.json#Figure S15(c)figure_digitization.json#Figure S15(d)figure_digitization.json#Figure S15(e)figure_digitization.json#Figure S17figure_digitization.json#Figure S2figure_digitization.json#Figure S4(c)figure_digitization.json#Figure S5(a)figure_digitization.json#Figure S5(b)figure_digitization.json#Figure S5(c)figure_digitization.json#Figure S5(d)figure_digitization.json#Figure S5(e)figure_digitization.json#Figure S5(f)figure_digitization.json#Figure S6(a)figure_digitization.json#Figure S6(b)figure_digitization.json#Figure S7figure_digitization.json#Figure S9(a)figure_digitization.json#Figure S9(c)figure_digitization.json#Figure S9(b)figure_digitization.json#Figure S9(d)figure_digitization.json#Figure 2figure_digitization.json#Figure S12figure_digitization.json#Figure S14(c)figure_digitization.json#Figure S15(a)figure_digitization.json#Figure S15(b)figure_digitization.json#Figure S15(c)figure_digitization.json#Figure S15(d)figure_digitization.json#Figure S15(e)figure_digitization.json#Figure S17figure_digitization.json#Figure S2figure_digitization.json#Figure S4(c)figure_digitization.json#Figure S5(a)figure_digitization.json#Figure S5(b)figure_digitization.json#Figure S5(c)figure_digitization.json#Figure S5(d)figure_digitization.json#Figure S5(e)figure_digitization.json#Figure S5(f)figure_digitization.json#Figure S6(a)figure_digitization.json#Figure S6(b)figure_digitization.json#Figure S7figure_digitization.json#Figure S9(a)figure_digitization.json#Figure S9(c)figure_digitization.json#Figure S9(b)figure_digitization.json#Figure S9(d)figure_digitization.json#Figure 2figure_digitization.json#Figure S12figure_digitization.json#Figure S14(c)figure_digitization.json#Figure S15(a)figure_digitization.json#Figure S15(b)figure_digitization.json#Figure S15(c)figure_digitization.json#Figure S15(d)figure_digitization.json#Figure S15(e)figure_digitization.json#Figure S17figure_digitization.json#Figure S2figure_digitization.json#Figure S4(c)figure_digitization.json#Figure S5(a)figure_digitization.json#Figure S5(b)figure_digitization.json#Figure S5(c)figure_digitization.json#Figure S5(d)figure_digitization.json#Figure S5(e)figure_digitization.json#Figure S5(f)figure_digitization.json#Figure S6(a)figure_digitization.json#Figure S6(b)figure_digitization.json#Figure S7figure_digitization.json#Figure S9(a)figure_digitization.json#Figure S9(c)figure_digitization.json#Figure S9(b)figure_digitization.json#Figure S9(d)figure_digitization.json#Figure 2figure_digitization.json#Figure S12figure_digitization.json#Figure S14(c)figure_digitization.json#Figure S15(a)figure_digitization.json#Figure S15(b)figure_digitization.json#Figure S15(c)figure_digitization.json#Figure S15(d)figure_digitization.json#Figure S15(e)figure_digitization.json#Figure S17figure_digitization.json#Figure S2figure_digitization.json#Figure S4(c)figure_digitization.json#Figure S5(a)figure_digitization.json#Figure S5(b)figure_digitization.json#Figure S5(c)figure_digitization.json#Figure S5(d)figure_digitization.json#Figure S5(e)figure_digitization.json#Figure S5(f)figure_digitization.json#Figure S6(a)figure_digitization.json#Figure S6(b)figure_digitization.json#Figure S7figure_digitization.json#Figure S9(a)figure_digitization.json#Figure S9(c)figure_digitization.json#Figure S9(b)figure_digitization.json#Figure S9(d)