| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| Raman Peak Separation | E2g-A1g separation | 24cm⁻¹ | — | |||
| Raman Peak Separation | E2g-A1g separation | 21cm⁻¹ | — | |||
| Raman Peak Separation | E2g-A1g separation | 19.5cm⁻¹ | — | |||
| Raman Peak Intensity | E2g intensity | ~50% reduction | — | |||
| Raman Peak Intensity | A1g intensity | ~50% reduction | — | |||
| Pl Peak Intensity Ratio | trion/A-exciton | 0.7 | — | |||
| Pl Peak Intensity Ratio | trion/A-exciton | 0.9 | — | |||
| Defect Density | S defect density | 560000000000000cm⁻² | — | |||
| Xps Binding Energy Shift | Mo 3d | 0.6eV | — | |||
| Xps Peak Area Ratio | S 2s | 0.42 | — | |||
| Xps Peak Area Ratio | S 2s | 0.32 | — | |||
| Xps Binding Energy | Mo 3d5/2 | 230.03eV | — | |||
| Xps Binding Energy | Mo 3d3/2 | 233.15eV | — | |||
| Xps Binding Energy | S 2s | 227.1eV | — | — | ||
| Xps Binding Energy | Mo 3d | 0.6eV | — | |||
| Xps Binding Energy | Mo 3d | 232.14eV | — | |||
| Xps Binding Energy | Mo 3d | 235.49eV | — |
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| Raman Peak Separation | E2g-A1g separation | 24cm⁻¹ | — | |||
| Raman Peak Separation | E2g-A1g separation | 21cm⁻¹ | — | |||
| Raman Peak Separation | E2g-A1g separation | 19.5cm⁻¹ | — | |||
| Raman Peak Intensity | E2g intensity | ~50% reduction | — | |||
| Raman Peak Intensity | A1g intensity | ~50% reduction | — | |||
| Pl Peak Intensity Ratio | trion/A-exciton | 0.7 | — | |||
| Pl Peak Intensity Ratio | trion/A-exciton | 0.9 | — | |||
| Defect Density | S defect density | 560000000000000cm⁻² | — | |||
| Xps Binding Energy Shift | Mo 3d | 0.6eV | — | |||
| Xps Peak Area Ratio | S 2s | 0.42 | — | |||
| Xps Peak Area Ratio | S 2s | 0.32 | — | |||
| Xps Binding Energy | Mo 3d5/2 | 230.03eV | — | |||
| Xps Binding Energy | Mo 3d3/2 | 233.15eV | — | |||
| Xps Binding Energy | S 2s | 227.1eV | — | — | ||
| Xps Binding Energy | Mo 3d | 0.6eV | — | |||
| Xps Binding Energy | Mo 3d | 232.14eV | — | |||
| Xps Binding Energy | Mo 3d | 235.49eV | — |
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| Raman Peak Separation | E2g-A1g separation | 24cm⁻¹ | — | |||
| Raman Peak Separation | E2g-A1g separation | 21cm⁻¹ | — | |||
| Raman Peak Separation | E2g-A1g separation | 19.5cm⁻¹ | — | |||
| Raman Peak Intensity | E2g intensity | ~50% reduction | — | |||
| Raman Peak Intensity | A1g intensity | ~50% reduction | — | |||
| Pl Peak Intensity Ratio | trion/A-exciton | 0.7 | — | |||
| Pl Peak Intensity Ratio | trion/A-exciton | 0.9 | — | |||
| Defect Density | S defect density | 560000000000000cm⁻² | — | |||
| Xps Binding Energy Shift | Mo 3d | 0.6eV | — | |||
| Xps Peak Area Ratio | S 2s | 0.42 | — | |||
| Xps Peak Area Ratio | S 2s | 0.32 | — | |||
| Xps Binding Energy | Mo 3d5/2 | 230.03eV | — | |||
| Xps Binding Energy | Mo 3d3/2 | 233.15eV | — | |||
| Xps Binding Energy | S 2s | 227.1eV | — | — | ||
| Xps Binding Energy | Mo 3d | 0.6eV | — | |||
| Xps Binding Energy | Mo 3d | 232.14eV | — | |||
| Xps Binding Energy | Mo 3d | 235.49eV | — |
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| Raman Peak Separation | E2g-A1g separation | 24cm⁻¹ | — | |||
| Raman Peak Separation | E2g-A1g separation | 21cm⁻¹ | — | |||
| Raman Peak Separation | E2g-A1g separation | 19.5cm⁻¹ | — | |||
| Raman Peak Intensity | E2g intensity | ~50% reduction | — | |||
| Raman Peak Intensity | A1g intensity | ~50% reduction | — | |||
| Pl Peak Intensity Ratio | trion/A-exciton | 0.7 | — | |||
| Pl Peak Intensity Ratio | trion/A-exciton | 0.9 | — | |||
| Defect Density | S defect density | 560000000000000cm⁻² | — | |||
| Xps Binding Energy Shift | Mo 3d | 0.6eV | — | |||
| Xps Peak Area Ratio | S 2s | 0.42 | — | |||
| Xps Peak Area Ratio | S 2s | 0.32 | — | |||
| Xps Binding Energy | Mo 3d5/2 | 230.03eV | — | |||
| Xps Binding Energy | Mo 3d3/2 | 233.15eV | — | |||
| Xps Binding Energy | S 2s | 227.1eV | — | — | ||
| Xps Binding Energy | Mo 3d | 0.6eV | — | |||
| Xps Binding Energy | Mo 3d | 232.14eV | — | |||
| Xps Binding Energy | Mo 3d | 235.49eV | — |