US 10,066,141GRAPHENE SHEET COMBINING GRAPHITE FLAKE STRUCTURE AND ITS MANUFACTURING METHOD, AND SLURRY FOR MANUFACTURING THE SAME
Tung CHOU
US
Copyright © 2026 Matter42. All rights reserved.
Patent
Atlas literature
Patent
US 10,066,141Patent drawings and their descriptions. Click a drawing to enlarge it.
FIG. 1 is a flow chart of a manufacturing method of a graphene sheet combining graphite flake structure according to an embodiment of the invention; [0026]
FIGS. 2A to 2G are schematic diagrams showing the manufacturing procedures of the graphene sheet combining graphite flake structure according to the embodiment …
FIG. 3 is a flow chart of another manufacturing method of a graphene sheet combining graphite flake structure according to the embodiment of the invention; and …
FIG. 4 is a schematic diagram showing the graphene sheet combining graphite flake structure according to the embodiment of the invention viewing from an SEM …
Claims define the patent's legal scope. Independent claims stand alone; dependent claims (nested) narrow them. Click a claim to expand its dependents.
A graphene sheet combining graphite flake structure, consisting of: a graphite nanoplatelet material; and a graphene material mixed in the graphite nanoplatelet material, wherein the content of the graphene material is between 1% and 80% of the graphite nanoplatelet material. Currently amended
The graphene sheet combining graphite flake structure of claim 1, wherein the graphite nanoplatelet material comprises a plurality of graphite nanoplatelets, a size of the graphite nanoplatelets is between 5 p m and 200 p m, and a thickness of the graphite nanoplatelets is between 0.1 p m and 0.5 m. Original
The graphene sheet combining graphite flake structure of claim 1, wherein the graphene material comprises a plurality of graphenes, a size of the graphenes is between 1 pm and 50p m, and a thickness of the graphenes is between 0.002 p m and 0.02 pm. Original
The graphene sheet combining graphite flake structure of claim 1, wherein a thickness of the graphene sheet combining graphite flake structure is between 2 p m and 100 pm. Original
The graphene sheet combining graphite flake structure of claim 1, wherein the graphene sheet combining graphite flake structure is flexible. Original
A manufacturing method of a graphene sheet combining graphite flake structure, comprising following steps of: adding a graphite nanoplatelet material into a solvent and stirring to form a well-mixed solution, wherein a weight percentage of the graphite nanoplatelet material is between 0.1% and 10%; adding a graphene material in the solution and stirring to form a well-mixed slurry, wherein the content of the graphene material is between 1% and 80% of the graphite nanoplatelet material; Page 3 of 8 applying the slurry on an object and drying the slurry to form a graphite coating; and pressing the graphite coating to form the graphene sheet combining graphite flake structure. Withdrawn
The manufacturing method of claim 6, wherein a thickness of the graphite coating is between 10p m and 500 pm. Withdrawn
The manufacturing method of claim 6, wherein the solvent is water, dimethylformamide (DMF), tetrahydrofuran (T H F), ketones, alcohols, acetic acid acetate, or toluene. Withdrawn
The manufacturing method of claim 6, wherein a weight percentage of the graphite nanoplatelet material is between 0.2% and 10%. Withdrawn
1 1. The manufacturing method of claim 6, wherein the graphite nanoplatelet material comprises a plurality of graphite nanoplatelets, a size of the graphite nanoplatelets is between 5 m and 200 p m, and a thickness of the graphite nanoplatelets is between 0.1 p m and 0.5 pm. Withdrawn
The manufacturing method of claim 6, wherein the graphene material comprises a plurality of graphenes, a size of the graphenes is between 1 p m and 50p m, and a thickness of the graphenes is between 0. 002 m and 0.02 pm. Withdrawn
The manufacturing method of claim 6, wherein the slurry is applied by a coating method or a printing method. Page 4 of 8 Withdrawn
The manufacturing method of claim 6, wherein the applied slurry is dried at a temperature lower than 400 ° C for 1 minute to 24 hours. Withdrawn
The manufacturing method of claim 6, wherein a thickness of the graphene sheet combining graphite flake structure is between 2 p m and 100 pm. Withdrawn
The manufacturing method of claim 6, further comprising a step of: departing the graphene sheet combining graphite flake structure from the object. Withdrawn
The manufacturing method of claim 6, wherein the graphene sheet combining graphite flake structure is flexible. Withdrawn
A slurry for manufacturing a graphene sheet combining graphite flake structure, comprising: a solvent; a graphite nanoplatelet material comprising a plurality of graphite nanoplatelets; and a graphene material comprising a plurality of graphenes; wherein, the graphite nanoplatelet material and the graphene material are mixed in the solvent, a weight percentage of the graphite nanoplatelet material is between 0.1% and 10%, and the content of the graphene material is between 1% and 80% of the graphite nanoplatelet material. Withdrawn
The slurry of claim 19, wherein a weight percentage of the graphite nanoplatelet material is between 0.2% and 10%, a size of the graphite nanoplatelets is between 5g m and 200 p m, a thickness of the graphite nanoplatelets is between 0.1 p m and 0.5 g m, a size of Attorney Docket No.: 4459/1782PUS 1 Response to Office Action dated 14 Dec 2017 Page 5 of 8 the graphenes is between 1p m and 5 0pm, and a thickness of the graphenes is between 0. 002pm and 0.02 pm. Withdrawn
Layer stacks claimed or described, ordered top of device to substrate.
graphene sheet combining graphite flake structure
Materials described outside the worked examples.
graphite nanoplatelet material
graphene material
Additional fabrication and treatment steps described in the patent.
Measurements and analyses referenced in the patent, with their drawing references.
FIG. 4 is a schematic diagram showing the graphene sheet combining graphite flake structure according to the embodiment of the invention viewing from an SEM …
Performance values and ranges asserted in the specification or claims.
| Property | Value | Material |
|---|---|---|
Duration | 60–86400 s | — |
Duration | 5–30 minutes |
Related documents with shared materials, methods, properties, or citations.
Patent
Atlas literature
Patent
US 10,066,141Patent drawings and their descriptions. Click a drawing to enlarge it.
FIG. 1 is a flow chart of a manufacturing method of a graphene sheet combining graphite flake structure according to an embodiment of the invention; [0026]
FIGS. 2A to 2G are schematic diagrams showing the manufacturing procedures of the graphene sheet combining graphite flake structure according to the embodiment …
FIG. 3 is a flow chart of another manufacturing method of a graphene sheet combining graphite flake structure according to the embodiment of the invention; and …
FIG. 4 is a schematic diagram showing the graphene sheet combining graphite flake structure according to the embodiment of the invention viewing from an SEM …
Claims define the patent's legal scope. Independent claims stand alone; dependent claims (nested) narrow them. Click a claim to expand its dependents.
A graphene sheet combining graphite flake structure, consisting of: a graphite nanoplatelet material; and a graphene material mixed in the graphite nanoplatelet material, wherein the content of the graphene material is between 1% and 80% of the graphite nanoplatelet material. Currently amended
The graphene sheet combining graphite flake structure of claim 1, wherein the graphite nanoplatelet material comprises a plurality of graphite nanoplatelets, a size of the graphite nanoplatelets is between 5 p m and 200 p m, and a thickness of the graphite nanoplatelets is between 0.1 p m and 0.5 m. Original
The graphene sheet combining graphite flake structure of claim 1, wherein the graphene material comprises a plurality of graphenes, a size of the graphenes is between 1 pm and 50p m, and a thickness of the graphenes is between 0.002 p m and 0.02 pm. Original
The graphene sheet combining graphite flake structure of claim 1, wherein a thickness of the graphene sheet combining graphite flake structure is between 2 p m and 100 pm. Original
The graphene sheet combining graphite flake structure of claim 1, wherein the graphene sheet combining graphite flake structure is flexible. Original
A manufacturing method of a graphene sheet combining graphite flake structure, comprising following steps of: adding a graphite nanoplatelet material into a solvent and stirring to form a well-mixed solution, wherein a weight percentage of the graphite nanoplatelet material is between 0.1% and 10%; adding a graphene material in the solution and stirring to form a well-mixed slurry, wherein the content of the graphene material is between 1% and 80% of the graphite nanoplatelet material; Page 3 of 8 applying the slurry on an object and drying the slurry to form a graphite coating; and pressing the graphite coating to form the graphene sheet combining graphite flake structure. Withdrawn
The manufacturing method of claim 6, wherein a thickness of the graphite coating is between 10p m and 500 pm. Withdrawn
The manufacturing method of claim 6, wherein the solvent is water, dimethylformamide (DMF), tetrahydrofuran (T H F), ketones, alcohols, acetic acid acetate, or toluene. Withdrawn
The manufacturing method of claim 6, wherein a weight percentage of the graphite nanoplatelet material is between 0.2% and 10%. Withdrawn
1 1. The manufacturing method of claim 6, wherein the graphite nanoplatelet material comprises a plurality of graphite nanoplatelets, a size of the graphite nanoplatelets is between 5 m and 200 p m, and a thickness of the graphite nanoplatelets is between 0.1 p m and 0.5 pm. Withdrawn
The manufacturing method of claim 6, wherein the graphene material comprises a plurality of graphenes, a size of the graphenes is between 1 p m and 50p m, and a thickness of the graphenes is between 0. 002 m and 0.02 pm. Withdrawn
The manufacturing method of claim 6, wherein the slurry is applied by a coating method or a printing method. Page 4 of 8 Withdrawn
The manufacturing method of claim 6, wherein the applied slurry is dried at a temperature lower than 400 ° C for 1 minute to 24 hours. Withdrawn
The manufacturing method of claim 6, wherein a thickness of the graphene sheet combining graphite flake structure is between 2 p m and 100 pm. Withdrawn
The manufacturing method of claim 6, further comprising a step of: departing the graphene sheet combining graphite flake structure from the object. Withdrawn
The manufacturing method of claim 6, wherein the graphene sheet combining graphite flake structure is flexible. Withdrawn
A slurry for manufacturing a graphene sheet combining graphite flake structure, comprising: a solvent; a graphite nanoplatelet material comprising a plurality of graphite nanoplatelets; and a graphene material comprising a plurality of graphenes; wherein, the graphite nanoplatelet material and the graphene material are mixed in the solvent, a weight percentage of the graphite nanoplatelet material is between 0.1% and 10%, and the content of the graphene material is between 1% and 80% of the graphite nanoplatelet material. Withdrawn
The slurry of claim 19, wherein a weight percentage of the graphite nanoplatelet material is between 0.2% and 10%, a size of the graphite nanoplatelets is between 5g m and 200 p m, a thickness of the graphite nanoplatelets is between 0.1 p m and 0.5 g m, a size of Attorney Docket No.: 4459/1782PUS 1 Response to Office Action dated 14 Dec 2017 Page 5 of 8 the graphenes is between 1p m and 5 0pm, and a thickness of the graphenes is between 0. 002pm and 0.02 pm. Withdrawn
Layer stacks claimed or described, ordered top of device to substrate.
graphene sheet combining graphite flake structure
Materials described outside the worked examples.
graphite nanoplatelet material
graphene material
Additional fabrication and treatment steps described in the patent.
Measurements and analyses referenced in the patent, with their drawing references.
FIG. 4 is a schematic diagram showing the graphene sheet combining graphite flake structure according to the embodiment of the invention viewing from an SEM …
Performance values and ranges asserted in the specification or claims.
| Property | Value | Material |
|---|---|---|
Duration | 60–86400 s | — |
Duration | 5–30 minutes |
Related documents with shared materials, methods, properties, or citations.
Patent
Atlas literature
Patent
US 10,066,141Patent drawings and their descriptions. Click a drawing to enlarge it.
FIG. 1 is a flow chart of a manufacturing method of a graphene sheet combining graphite flake structure according to an embodiment of the invention; [0026]
FIGS. 2A to 2G are schematic diagrams showing the manufacturing procedures of the graphene sheet combining graphite flake structure according to the embodiment …
FIG. 3 is a flow chart of another manufacturing method of a graphene sheet combining graphite flake structure according to the embodiment of the invention; and …
FIG. 4 is a schematic diagram showing the graphene sheet combining graphite flake structure according to the embodiment of the invention viewing from an SEM …
Claims define the patent's legal scope. Independent claims stand alone; dependent claims (nested) narrow them. Click a claim to expand its dependents.
A graphene sheet combining graphite flake structure, consisting of: a graphite nanoplatelet material; and a graphene material mixed in the graphite nanoplatelet material, wherein the content of the graphene material is between 1% and 80% of the graphite nanoplatelet material. Currently amended
The graphene sheet combining graphite flake structure of claim 1, wherein the graphite nanoplatelet material comprises a plurality of graphite nanoplatelets, a size of the graphite nanoplatelets is between 5 p m and 200 p m, and a thickness of the graphite nanoplatelets is between 0.1 p m and 0.5 m. Original
The graphene sheet combining graphite flake structure of claim 1, wherein the graphene material comprises a plurality of graphenes, a size of the graphenes is between 1 pm and 50p m, and a thickness of the graphenes is between 0.002 p m and 0.02 pm. Original
The graphene sheet combining graphite flake structure of claim 1, wherein a thickness of the graphene sheet combining graphite flake structure is between 2 p m and 100 pm. Original
The graphene sheet combining graphite flake structure of claim 1, wherein the graphene sheet combining graphite flake structure is flexible. Original
A manufacturing method of a graphene sheet combining graphite flake structure, comprising following steps of: adding a graphite nanoplatelet material into a solvent and stirring to form a well-mixed solution, wherein a weight percentage of the graphite nanoplatelet material is between 0.1% and 10%; adding a graphene material in the solution and stirring to form a well-mixed slurry, wherein the content of the graphene material is between 1% and 80% of the graphite nanoplatelet material; Page 3 of 8 applying the slurry on an object and drying the slurry to form a graphite coating; and pressing the graphite coating to form the graphene sheet combining graphite flake structure. Withdrawn
The manufacturing method of claim 6, wherein a thickness of the graphite coating is between 10p m and 500 pm. Withdrawn
The manufacturing method of claim 6, wherein the solvent is water, dimethylformamide (DMF), tetrahydrofuran (T H F), ketones, alcohols, acetic acid acetate, or toluene. Withdrawn
The manufacturing method of claim 6, wherein a weight percentage of the graphite nanoplatelet material is between 0.2% and 10%. Withdrawn
1 1. The manufacturing method of claim 6, wherein the graphite nanoplatelet material comprises a plurality of graphite nanoplatelets, a size of the graphite nanoplatelets is between 5 m and 200 p m, and a thickness of the graphite nanoplatelets is between 0.1 p m and 0.5 pm. Withdrawn
The manufacturing method of claim 6, wherein the graphene material comprises a plurality of graphenes, a size of the graphenes is between 1 p m and 50p m, and a thickness of the graphenes is between 0. 002 m and 0.02 pm. Withdrawn
The manufacturing method of claim 6, wherein the slurry is applied by a coating method or a printing method. Page 4 of 8 Withdrawn
The manufacturing method of claim 6, wherein the applied slurry is dried at a temperature lower than 400 ° C for 1 minute to 24 hours. Withdrawn
The manufacturing method of claim 6, wherein a thickness of the graphene sheet combining graphite flake structure is between 2 p m and 100 pm. Withdrawn
The manufacturing method of claim 6, further comprising a step of: departing the graphene sheet combining graphite flake structure from the object. Withdrawn
The manufacturing method of claim 6, wherein the graphene sheet combining graphite flake structure is flexible. Withdrawn
A slurry for manufacturing a graphene sheet combining graphite flake structure, comprising: a solvent; a graphite nanoplatelet material comprising a plurality of graphite nanoplatelets; and a graphene material comprising a plurality of graphenes; wherein, the graphite nanoplatelet material and the graphene material are mixed in the solvent, a weight percentage of the graphite nanoplatelet material is between 0.1% and 10%, and the content of the graphene material is between 1% and 80% of the graphite nanoplatelet material. Withdrawn
The slurry of claim 19, wherein a weight percentage of the graphite nanoplatelet material is between 0.2% and 10%, a size of the graphite nanoplatelets is between 5g m and 200 p m, a thickness of the graphite nanoplatelets is between 0.1 p m and 0.5 g m, a size of Attorney Docket No.: 4459/1782PUS 1 Response to Office Action dated 14 Dec 2017 Page 5 of 8 the graphenes is between 1p m and 5 0pm, and a thickness of the graphenes is between 0. 002pm and 0.02 pm. Withdrawn
Layer stacks claimed or described, ordered top of device to substrate.
graphene sheet combining graphite flake structure
Materials described outside the worked examples.
graphite nanoplatelet material
graphene material
Additional fabrication and treatment steps described in the patent.
Measurements and analyses referenced in the patent, with their drawing references.
FIG. 4 is a schematic diagram showing the graphene sheet combining graphite flake structure according to the embodiment of the invention viewing from an SEM …
Performance values and ranges asserted in the specification or claims.
| Property | Value | Material |
|---|---|---|
Duration | 60–86400 s | — |
Duration | 5–30 minutes |
Related documents with shared materials, methods, properties, or citations.
Patent
Atlas literature
Patent
US 10,066,141Patent drawings and their descriptions. Click a drawing to enlarge it.
FIG. 1 is a flow chart of a manufacturing method of a graphene sheet combining graphite flake structure according to an embodiment of the invention; [0026]
FIGS. 2A to 2G are schematic diagrams showing the manufacturing procedures of the graphene sheet combining graphite flake structure according to the embodiment …
FIG. 3 is a flow chart of another manufacturing method of a graphene sheet combining graphite flake structure according to the embodiment of the invention; and …
FIG. 4 is a schematic diagram showing the graphene sheet combining graphite flake structure according to the embodiment of the invention viewing from an SEM …
Claims define the patent's legal scope. Independent claims stand alone; dependent claims (nested) narrow them. Click a claim to expand its dependents.
A graphene sheet combining graphite flake structure, consisting of: a graphite nanoplatelet material; and a graphene material mixed in the graphite nanoplatelet material, wherein the content of the graphene material is between 1% and 80% of the graphite nanoplatelet material. Currently amended
The graphene sheet combining graphite flake structure of claim 1, wherein the graphite nanoplatelet material comprises a plurality of graphite nanoplatelets, a size of the graphite nanoplatelets is between 5 p m and 200 p m, and a thickness of the graphite nanoplatelets is between 0.1 p m and 0.5 m. Original
The graphene sheet combining graphite flake structure of claim 1, wherein the graphene material comprises a plurality of graphenes, a size of the graphenes is between 1 pm and 50p m, and a thickness of the graphenes is between 0.002 p m and 0.02 pm. Original
The graphene sheet combining graphite flake structure of claim 1, wherein a thickness of the graphene sheet combining graphite flake structure is between 2 p m and 100 pm. Original
The graphene sheet combining graphite flake structure of claim 1, wherein the graphene sheet combining graphite flake structure is flexible. Original
A manufacturing method of a graphene sheet combining graphite flake structure, comprising following steps of: adding a graphite nanoplatelet material into a solvent and stirring to form a well-mixed solution, wherein a weight percentage of the graphite nanoplatelet material is between 0.1% and 10%; adding a graphene material in the solution and stirring to form a well-mixed slurry, wherein the content of the graphene material is between 1% and 80% of the graphite nanoplatelet material; Page 3 of 8 applying the slurry on an object and drying the slurry to form a graphite coating; and pressing the graphite coating to form the graphene sheet combining graphite flake structure. Withdrawn
The manufacturing method of claim 6, wherein a thickness of the graphite coating is between 10p m and 500 pm. Withdrawn
The manufacturing method of claim 6, wherein the solvent is water, dimethylformamide (DMF), tetrahydrofuran (T H F), ketones, alcohols, acetic acid acetate, or toluene. Withdrawn
The manufacturing method of claim 6, wherein a weight percentage of the graphite nanoplatelet material is between 0.2% and 10%. Withdrawn
1 1. The manufacturing method of claim 6, wherein the graphite nanoplatelet material comprises a plurality of graphite nanoplatelets, a size of the graphite nanoplatelets is between 5 m and 200 p m, and a thickness of the graphite nanoplatelets is between 0.1 p m and 0.5 pm. Withdrawn
The manufacturing method of claim 6, wherein the graphene material comprises a plurality of graphenes, a size of the graphenes is between 1 p m and 50p m, and a thickness of the graphenes is between 0. 002 m and 0.02 pm. Withdrawn
The manufacturing method of claim 6, wherein the slurry is applied by a coating method or a printing method. Page 4 of 8 Withdrawn
The manufacturing method of claim 6, wherein the applied slurry is dried at a temperature lower than 400 ° C for 1 minute to 24 hours. Withdrawn
The manufacturing method of claim 6, wherein a thickness of the graphene sheet combining graphite flake structure is between 2 p m and 100 pm. Withdrawn
The manufacturing method of claim 6, further comprising a step of: departing the graphene sheet combining graphite flake structure from the object. Withdrawn
The manufacturing method of claim 6, wherein the graphene sheet combining graphite flake structure is flexible. Withdrawn
A slurry for manufacturing a graphene sheet combining graphite flake structure, comprising: a solvent; a graphite nanoplatelet material comprising a plurality of graphite nanoplatelets; and a graphene material comprising a plurality of graphenes; wherein, the graphite nanoplatelet material and the graphene material are mixed in the solvent, a weight percentage of the graphite nanoplatelet material is between 0.1% and 10%, and the content of the graphene material is between 1% and 80% of the graphite nanoplatelet material. Withdrawn
The slurry of claim 19, wherein a weight percentage of the graphite nanoplatelet material is between 0.2% and 10%, a size of the graphite nanoplatelets is between 5g m and 200 p m, a thickness of the graphite nanoplatelets is between 0.1 p m and 0.5 g m, a size of Attorney Docket No.: 4459/1782PUS 1 Response to Office Action dated 14 Dec 2017 Page 5 of 8 the graphenes is between 1p m and 5 0pm, and a thickness of the graphenes is between 0. 002pm and 0.02 pm. Withdrawn
Layer stacks claimed or described, ordered top of device to substrate.
graphene sheet combining graphite flake structure
Materials described outside the worked examples.
graphite nanoplatelet material
graphene material
Additional fabrication and treatment steps described in the patent.
Measurements and analyses referenced in the patent, with their drawing references.
FIG. 4 is a schematic diagram showing the graphene sheet combining graphite flake structure according to the embodiment of the invention viewing from an SEM …
Performance values and ranges asserted in the specification or claims.
| Property | Value | Material |
|---|---|---|
Duration | 60–86400 s | — |
Duration | 5–30 minutes |
Related documents with shared materials, methods, properties, or citations.
slurry (graphite nanoplatelet + graphene in solvent)
solvent
FIG. 4 is a schematic diagram showing the graphene sheet combining graphite flake structure according to the embodiment of the invention viewing from an SEM …
| — |
slurry (graphite nanoplatelet + graphene in solvent)
solvent
FIG. 4 is a schematic diagram showing the graphene sheet combining graphite flake structure according to the embodiment of the invention viewing from an SEM …
| — |
slurry (graphite nanoplatelet + graphene in solvent)
solvent
FIG. 4 is a schematic diagram showing the graphene sheet combining graphite flake structure according to the embodiment of the invention viewing from an SEM …
| — |
slurry (graphite nanoplatelet + graphene in solvent)
solvent
FIG. 4 is a schematic diagram showing the graphene sheet combining graphite flake structure according to the embodiment of the invention viewing from an SEM …
| — |