Research paper
Experimental CharacterizationBlister Test to Measure the Out-of-Plane Shear Modulus of Few-Layer Graphene
Metehan Calis, Narasimha Boddeti, J. Scott Bunch
Copyright © 2026 Matter42. All rights reserved.
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| Layer Thickness | MoS₂ monolayer thickness | 0.65nm | — | |||
| Shear Modulus | out-of-plane shear modulus | 0.97GPa | — | |||
| Adhesion Energy | separation energy | 0.2J/m² | — |
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| Layer Thickness | MoS₂ monolayer thickness | 0.65nm | — | |||
| Shear Modulus | out-of-plane shear modulus | 0.97GPa | — | |||
| Adhesion Energy | separation energy | 0.2J/m² | — |
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| Layer Thickness | MoS₂ monolayer thickness | 0.65nm | — | |||
| Shear Modulus | out-of-plane shear modulus | 0.97GPa | — | |||
| Adhesion Energy | separation energy | 0.2J/m² | — |
| Type | Label | Value | Material | Sample | Condition | Source |
|---|---|---|---|---|---|---|
| Layer Thickness | MoS₂ monolayer thickness | 0.65nm | — | |||
| Shear Modulus | out-of-plane shear modulus | 0.97GPa | — | |||
| Adhesion Energy | separation energy | 0.2J/m² | — |
figure_digitization.json#Figure S1(b)figure_digitization.json#Figure S1(a)figure_digitization.json#Figure S1(b)figure_digitization.json#Figure S1(a)figure_digitization.json#Figure S7(b)figure_digitization.json#Figure S7(c)figure_digitization.json#Figure S7(d)figure_digitization.json#Figure S7(e)figure_digitization.json#Figure S7(f)figure_digitization.json#Figure S1(b)figure_digitization.json#Figure S1(a)figure_digitization.json#Figure S1(b)figure_digitization.json#Figure S1(a)figure_digitization.json#Figure S7(b)figure_digitization.json#Figure S7(c)figure_digitization.json#Figure S7(d)figure_digitization.json#Figure S7(e)figure_digitization.json#Figure S7(f)figure_digitization.json#Figure S1(b)figure_digitization.json#Figure S1(a)figure_digitization.json#Figure S1(b)figure_digitization.json#Figure S1(a)figure_digitization.json#Figure S7(b)figure_digitization.json#Figure S7(c)figure_digitization.json#Figure S7(d)figure_digitization.json#Figure S7(e)figure_digitization.json#Figure S7(f)figure_digitization.json#Figure S1(b)figure_digitization.json#Figure S1(a)figure_digitization.json#Figure S1(b)figure_digitization.json#Figure S1(a)figure_digitization.json#Figure S7(b)figure_digitization.json#Figure S7(c)figure_digitization.json#Figure S7(d)figure_digitization.json#Figure S7(e)figure_digitization.json#Figure S7(f)